| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 1700 MPa | - |
| Tensile strength at yield | ISO 527-1 | 44 MPa | - |
| Tensile stress at break | ISO 527-1 | 46 MPa | Typical |
| Elongation at break | ISO 527-1 | 220 % | Typical |
| Flexural modulus | ISO 178 | 1600 MPa | - |
| Flexural strength | ISO 178 | 60 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 100 | Outstanding |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 50 kJ/m² | Good |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 76 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 64 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 84 | Good |
| Melting point (Tm) | ISO 3146-C | Amorphous (no Tm) {ISO 3146-C} | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 85 (unconfirmed) (ISO 11357-1 (DSC)) | - |
| Thermal decomposition temp. | - | 370 °C | - |
| CLTE — flow direction | - | 0.7 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.23 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.5 % | - |
| Mould shrinkage | ISO 294-4 | 0.2–0.5 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| UV resistance | - | Good | - |
| Chemical resistance | - | Very Good | - |