| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 1500 MPa | - |
| Tensile strength at yield | ISO 527-1 | 50 MPa | - |
| Elongation at break | ISO 527-1 | > 50 % | - |
| Flexural modulus | ISO 178 | 1300 MPa | - |
| Flexural strength | ISO 178 | 45 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 11 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 6 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 60 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 4800 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 135 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 55 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 142 °C | - |
| Melting point (Tm) | ISO 3146-C | 180 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 45 °C | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 8 cm³/10 min | Good |
| Thermal decomposition temp. | - | > 300 °C | - |
| CLTE — flow direction | - | 0.0001 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.01 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 1.6 % | Typical |
| Mould shrinkage | ISO 294-4 | 1 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (1.6 mm) (UL94) | - |
| Chemical resistance | - | Good | - |
| Electrical Properties | Method | Value | Rating |
|---|---|---|---|
| Specific surface resistance | - | 100000000000000 Ω | - |
| Specific volume resistivity | - | 100000000000000 Ω·cm | - |
| Dielectric strength | - | 30 kV/mm | - |
| Comparative tracking index (CTI) | - | 600 V | - |