UP TO 1000 MM/S| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 2300 MPa | - |
| Tensile strength at yield | ISO 527-1 | 48 MPa | - |
| Elongation at break | ISO 527-1 | 14 % | Typical |
| Flexural modulus | ISO 178 | 2200 MPa | - |
| Flexural strength | ISO 178 | 74 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 12 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 5 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 80 kJ/m² | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 50 kJ/m² | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 15 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 3000 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 92 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 80 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 96 °C | - |
| Melting point (Tm) | ISO 3146-C | Amorphous (no Tm) {ISO 3146-C} | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 103 °C | - |
| Melt flow rate (MFR) — 210°C/2.16 kg | - | 4 g/10 min {ISO 1133-1 | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 25 cm³/10 min | Very Good |
| Thermal decomposition temp. | - | 350 °C | - |
| CLTE — flow direction | - | 0.9 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.1 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.8 % | - |
| Mould shrinkage | ISO 294-4 | 0.4–0.7 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (UL94) | - |
| UV resistance | - | Very Good | - |
| Chemical resistance | - | Good | - |
| Flame retardant rating 3,0mm | - | HB (UL94) | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | HB | - |