In Stock
| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 3217 MPa | - |
| Tensile strength at yield | ISO 527-1 | 56.9 MPa | - |
| Tensile stress at break | ISO 527-1 | 8.2 MPa | - |
| Elongation at break | ISO 527-1 | 12 % | Typical |
| Flexural modulus | ISO 178 | 3339 MPa | - |
| Flexural strength | ISO 178 | 89.8 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 4.9 kJ/m² | Typical |
| Charpy notched impact strength (-30°C) | - | 3–4 | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/A) — 1.8 MPa | - | 65 °C | - |
| Vicat softening temp. (VST/B50) | - | 159 °C | - |
| Melting point (Tm) | ISO 3146-C | 176 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 58 °C | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 5.81 cm³/10 min | Typical |