Tensile modulus (Young's modulus)

Test/Property Method

Test/Property Numeric Value

Test/Property Unit

2400 MPa (ISO 527–1)

Tensile strength at yield

Test/Property Comparable

Test/Property Max Value

Test/Property Min Value

Test/Property Note

Test/Property Tolerance Type

Test/Property Tolerance Value

55 MPa (ISO 527)

Tensile stress at break

Elongation at break

3.8 % (ISO 527–2)

Flexural modulus

Charpy notched impact strength (+23°C)

18 kJ/m² (ISO 179/1eA)

Vicat softening temp. (VST/B50)

Melting point (Tm)

179–183 °C

Melt flow rate (MFR) — 210°C/2.16 kg

Density

1.21 g/cm³ (ISO 1183)

Mould shrinkage

0.6% (parallel) / 0.9% (normal) % (ISO 294–4)

Nozzle temperature

270–300 °C

Build plate temperature

80–100 °C

Surface preparation

Print speed

20–150 mm/s

Cooling fan

10–40 %

Enclosed chamber required

Hardened nozzle required

Max. volumetric flow rate

10–18 mm³/s

Drying temperature

65 °C

Drying time

8–12 h

Flexural strength

Heat deflection temp. (HDT/B) — 0.45 MPa

210 °C (ISO 75–2/B)

Thermal decomposition temp.

~> 300 °C

Flame retardant rating

UV resistance

Chemical resistance

Very Good

Abrasion resistance

ESD safe

Flammability rating (UL 94)

Charpy notched impact strength (-30°C)

Charpy unnotched impact strength (-30°C)

Heat deflection temp. (HDT/A) — 1.8 MPa

95 °C (ISO 75–2/A)

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

No Break (NB) kJ/m² (ISO 179/1eU)

Puncture maximum force (-30°C)

Multiaxial instrumented impact, peak force (-30°C)

Melt volume rate (MVR) — 235°C/5.0 kg

CLTE — flow direction

Water absorption (saturation, 23°C)

0.09 % (ISO 62)

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

Filaments

Engineering

Material

DuraPro PA6 GF

Color

black

Filament diameter

1.75 mm

Coil

0.8 kg

DuraPro PA6 GF black 1.75 mm 0.8 kg

DuraPro PA6
GF is a glass fiber reinforced, highly functional polyamide designed for
demanding industrial applications. It is characterized by excellent mechanical
properties, enhanced heat resistance and reduced warping behavior, as well as
very good chemical resistance. The glass fiber reinforcement enables improved
tensile strength and high stiffness, while its higher moisture absorption
contributes to increased impact resistance.

Filament

DuraPro PA6 GF is a glass fiber reinforced polyamide filament offering high strength, stiffness, heat resistance, and low warping. Ideal for industrial applications.