Tensile modulus (Young's modulus)

Test/Property Method

Test/Property Numeric Value

Test/Property Unit

3500 MPa (ISO 527–1/-2)

Tensile strength at yield

50 MPa (ISO 527–1/-2)

Tensile stress at break

Elongation at break

5 % (ISO 527–1/-2)

Flexural modulus

Charpy notched impact strength (+23°C)

Vicat softening temp. (VST/B50)

Melting point (Tm)

175 °C (ISO 11357–3 (DSC))

Melt flow rate (MFR) — 210°C/2.16 kg

23 g/10 min (ISO 1133–1 (210 °C/2.16 kg))

Density

1.24 g/cm³ (ISO 1183–1)

Mould shrinkage

Nozzle temperature

Test/Property Max Value

< 250 °C

Build plate temperature

Test/Property Comparable

Test/Property Min Value

Test/Property Note

Test/Property Tolerance Type

Test/Property Tolerance Value

20–60 °C

Surface preparation

Not required

Print speed

< 1000 mm/s

Cooling fan

30–100 %

Enclosed chamber required

Hardened nozzle required

Max. volumetric flow rate

21 mm³/s

Drying temperature

50 °C

Drying time

0–6 h

Flexural strength

Heat deflection temp. (HDT/B) — 0.45 MPa

60 °C (ISO 75–2/B)

Thermal decomposition temp.

Flame retardant rating

UV resistance

Chemical resistance

Abrasion resistance

ESD safe

Flammability rating (UL 94)

Charpy notched impact strength (-30°C)

Charpy unnotched impact strength (-30°C)

Heat deflection temp. (HDT/A) — 1.8 MPa

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

Puncture maximum force (-30°C)

Multiaxial instrumented impact, peak force (-30°C)

Melt volume rate (MVR) — 235°C/5.0 kg

CLTE — flow direction

Water absorption (saturation, 23°C)

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

60 °C (ISO 11357–1 (DSC))

Filaments

Standard

Material

PLA HS

Color

black

Filament diameter

1.75 mm

Coil

1 kg

PLA HS black 1.75 mm 1 kg

Extrudr PLA High Speed is a specifically designed filament for fast 3D printing. It enables more precise and detailed printing results at far higher speeds than standard PLA. Its superior flow characteristics and rapid cooling make it perfect for applications that require both efficiency and high quality, such as prototyping, design concept visualization, decorative objects, and functional parts.&nbsp;&nbsp;

The material is easy to use, works reliably across various 3D printing environments, and delivers warp-free results for consistent and dependable prints – whether you're a beginner or an experienced user.&nbsp;

Filament

Ultra-fast PLA filament up to 1000 mm/s. Easy to print, strong, and reliable. Great for design, prototypes, and functional parts.

PLA High-Speed – Fast & Precise 3D Printing

white

PLA HS white 1.75 mm 1 kg

neon green

PLA HS neon green 1.75 mm 1 kg

neon orange

PLA HS neon orange 1.75 mm 1 kg

neon yellow

PLA HS neon yellow 1.75 mm 1 kg

hellfire red

PLA HS hellfire red 1.75 mm 1 kg

navy blue

PLA HS navy blue 1.75 mm 1 kg

anthracite

PLA HS anthracite 1.75 mm 1 kg

metallic

PLA HS metallic 1.75 mm 1 kg

silver

PLA HS silver 1.75 mm 1 kg

grey

PLA HS grey 1.75 mm 1 kg

military beige

PLA HS military beige 1.75 mm 1 kg

yellow

PLA HS yellow 1.75 mm 1 kg

orange

PLA HS orange 1.75 mm 1 kg

PLA HS red 1.75 mm 1 kg

light blue

PLA HS light blue 1.75 mm 1 kg

turquoise

PLA HS turquoise 1.75 mm 1 kg

military green

PLA HS military green 1.75 mm 1 kg

military dark green

PLA HS military dark green 1.75 mm 1 kg

brown

PLA HS brown 1.75 mm 1 kg

pastel green

PLA HS pastel green 1.75 mm 1 kg

pastel blue

PLA HS pastel blue 1.75 mm 1 kg

PLA HS

Matériau

couleur

Diamètre du filament

Bobine

numéro de produit

Chercher

PLA HS

Matériau

couleur

Diamètre du filament

Bobine

numéro de produit