Tensile modulus (Young's modulus)

Test/Property Comparable

Test/Property Max Value

Test/Property Method

Test/Property Min Value

Test/Property Note

Test/Property Numeric Value

Test/Property Tolerance Type

Test/Property Tolerance Value

Test/Property Unit

2500 MPa (ISO 527-1/-2)

Tensile strength at yield

34 MPa (ISO 527-1/-2)

Tensile stress at break

Elongation at break

6.9 % (ISO 527-1/-2)

Flexural modulus

1800 MPa (ISO 178)

Charpy notched impact strength (+23°C)

Vicat softening temp. (VST/B50)

58 °C (ISO 306/A50)

Melting point (Tm)

Melt flow rate (MFR) — 210°C/2.16 kg

4 g/10 min (ISO 1133-1 (210°C/2.16 kg))

Density

1.25 g/cm³ (ISO 2781)

Mould shrinkage

0.67 % (ISO 294-4)

Nozzle temperature

140–210 °C

Build plate temperature

20–60 °C

Surface preparation

Not required

Print speed

20–200 mm/s

Cooling fan

30–100 %

Enclosed chamber required

No yes/no

Hardened nozzle required

Max. volumetric flow rate

Drying temperature

50 °C

Drying time

Flexural strength

30.1 MPa (ISO 178)

Heat deflection temp. (HDT/B) — 0.45 MPa

51 °C (ISO 75-2/B)

Thermal decomposition temp.

Flame retardant rating

UV resistance

Chemical resistance

Abrasion resistance

ESD safe

Flammability rating (UL 94)

Charpy notched impact strength (-30°C)

Charpy unnotched impact strength (-30°C)

Heat deflection temp. (HDT/A) — 1.8 MPa

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

Puncture maximum force (-30°C)

Multiaxial instrumented impact, peak force (-30°C)

Melt volume rate (MVR) — 235°C/5.0 kg

CLTE — flow direction

Water absorption (saturation, 23°C)

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

Filaments

Specialty

Material

PEARL

Color

nature

Filament diameter

1.75 mm

Coil

1.1 kg

PEARL nature 1.75 mm 1.1 kg

PEARL comes from our BIO design range and impresses with its uniquely supple surface. The material consists of 100% renewable raw materials. The raw material is approved according to REACH, RoHS and FDA standards.

Filament

PEARL is a biodegradable design filament for 3D printing with a unique pearl look and supple surface. Made from 100% renewable raw materials, it offers excellent printing and flow properties, low warping, and is REACH, RoHS, and FDA compliant.