Name: FLEX Medium MATT - FLEX Medium MATT black 1.75 mm 0.75 kg
Brand: Extrudr
SKU: 9010241422029
Price: 39.98 EUR
Availability: OutOfStock

Imprint

Privacy Policy

Shipping

Faqs

Product Catalogue

Data Sheets

Material Profiles

Contact

Story

Career At Extrudr

Tensile modulus (Young's modulus)

Tensile strength at yield

Test/Property Method

Test/Property Numeric Value

Test/Property Unit

69 MPa (ISO 527–1/-2)

Tensile stress at break

Test/Property Comparable

Test/Property Max Value

Test/Property Min Value

Test/Property Note

Test/Property Tolerance Type

Test/Property Tolerance Value

52 MPa (DIN 53504, S1)

Elongation at break

470 % (ISO 527–1/-2)

Flexural modulus

Charpy notched impact strength (+23°C)

Vicat softening temp. (VST/B50)

Melting point (Tm)

Melt flow rate (MFR) — 210°C/2.16 kg

Density

1.15 g/cm³ (ISO 1183–1)

Mould shrinkage

Nozzle temperature

220–250 °C

Build plate temperature

50 °C

Surface preparation

Not required

Print speed

> 50 mm/s

Cooling fan

60–100 %

Enclosed chamber required

Hardened nozzle required

Max. volumetric flow rate

12 mm³/s

Drying temperature

60 °C

Drying time

12 h

Flexural strength

29 MPa (DIN 53504, S1)

Heat deflection temp. (HDT/B) — 0.45 MPa

Thermal decomposition temp.

Flame retardant rating

UV resistance

Chemical resistance

Abrasion resistance

30 mm³ (ISO 4649-A)

ESD safe

Flammability rating (UL 94)

Charpy notched impact strength (-30°C)

Charpy unnotched impact strength (-30°C)

Heat deflection temp. (HDT/A) — 1.8 MPa

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

Puncture maximum force (-30°C)

Multiaxial instrumented impact, peak force (-30°C)

Melt volume rate (MVR) — 235°C/5.0 kg

CLTE — flow direction

Water absorption (saturation, 23°C)

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

Filaments

Flexible

Material

FLEX Medium MATT

Color

black

Filament diameter

1.75 mm

Coil

0.75 kg

FLEX Medium MATT black 1.75 mm 0.75 kg

TPU FLEX Medium MATT is engineered for the FDM/FFF process and delivers the perfect balance of flexibility, strength, and style. With an extensibility of up to 470%, high chemical resistance, and a heat distortion resistance of up to 115 °C, the material is ideal for a wide range of industrial applications. In addition, the matte surface finish provides a refined and modern appearance, making it suitable not only for functional parts but also for aesthetic components. The raw material is compliant with REACH and RoHS standards.<br>

Filament

High-performance TPU FLEX Medium Matt filament with 470% extensibility, Shore A98, 115 °C resistance, extreme adhesion, and a refined matte finish.