DuraPro ASA was developed for industrial applications and offers tested UV and weather resistance, making it well suited to automotive and outdoor use. Independent weatherability testing shows only moderate colour change after 2000 hours of UV exposure. The material has strong mechanical resistance, good layer and bed adhesion, and low warping, with a matte surface finish. It is fire retardant to UL 94 HB.
Independently tested for UV and weather resistance, holding its colour and integrity through extended outdoor exposure.
Strong, durable, and built to withstand real mechanical stress in demanding environments.
Engineered for dimensional accuracy and reliable prints, even on larger industrial parts.
A precise, matte surface finish with a professional, technical look and feel.
From standard FDM printers to AMS and multi-material setups, Extrudr filament is built to work reliably with the printer you already own.
From the Austrian Alps, every Extrudr spool is manufactured with care, precision and strict EU standards.
DuraPro ASA is compatible with all standard FDM printers on the market. Note: an enclosed print space is required, and a heated bed capable of reaching 100–110°C is recommended.
No. DuraPro ASA prints reliably with a standard nozzle.
Yes. DuraPro ASA is fully compatible with AMS (Automatic Material System) solutions, including the Bambu Lab AMS.
Yes. DuraPro ASA is a hygroscopic material and should be dried before printing to achieve optimal print quality. We recommend drying for 10 hours at 60°C.
Yes. DuraPro ASA is specifically formulated for high UV and weather resistance, making it well suited to automotive and outdoor applications.
DuraPro ASA is compliant with FDA standards. Any printed item intended for food contact needs to be separately certified.
DuraPro ASA is rated UL 94 HB for flame retardancy.
Compliance applies to the raw material, not the finished printed part. Any part intended for a regulated application must undergo separate certification by an accredited third-party laboratory. Requirements vary depending on intended use and applicable standards.
Store DuraPro ASA in a dry room at room temperature (18–27°C / 65–80°F). Stored neatly, it is protected from dust and sunlight.
When stored correctly, DuraPro ASA has a shelf life of 2 years.
Tolles Material. Mit dem Profil für den Prusa Core gelingt ein Super Druck. Tolles Preisleistungsverhältnis. Inklusive der Zertifikate.
Tolles Material. Mit dem Profil für den Prusa Core gelingt ein Super Druck. Tolles Preisleistungsverhältnis. Inklusive der Zertifikate.
Sehr gutes Filament bei dem jede Spule gleichemäßige und hochwertige Ergebnisse liefert.
Sehr gutes Filament bei dem jede Spule gleichemäßige und hochwertige Ergebnisse liefert.
Très bon produit, délai de livraison trop long...
Très bon produit, délai de livraison trop long...
Beständige Qualität.
Beständige Qualität.
UP TO 1000 MM/S
Recommended settings for printers with a 0.4 mm nozzle. Max. 50% layer height. Optimal settings may vary between printers and are also dependent on environmental factors.
Our material profiles make printing easier and more reliable. The profiles are perfectly optimised for Extrudr filaments and deliver perfect results straight away. Simply select your printer and material, import the profile into your slicer, and you’re ready to go.
| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 2300 MPa | Excellent |
| Tensile strength at yield | ISO 527-1 | 48 MPa | Good |
| Elongation at break | ISO 527-1 | 14 % | Typical |
| Flexural modulus | ISO 178 | 2200 MPa | Excellent |
| Flexural strength | ISO 178 | 74 MPa | Very Good |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 12 kJ/m² | Very Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 5 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 80 kJ/m² | Very Good |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 50 kJ/m² | Very Good |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 15 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 3000 N | Very Good |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 92 °C | Very Good |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 80 °C | Good |
| Vicat softening temp. (VST/B50) | ISO 306 | 96 °C | Very Good |
| Melting point (Tm) | ISO 3146-C | Amorphous (no Tm) | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 103 °C | Excellent |
| Melt flow rate (MFR) — 210°C/2.16 kg | ISO 1133-1 (210°C/2.16 kg) | 4 g/10 min | Typical |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 25 cm³/10 min | Excellent |
| Thermal decomposition temp. | - | 350 °C | Excellent |
| CLTE — flow direction | - | 0.9 cm/cm/°C | Very Good |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.1 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.8 % | - |
| Mould shrinkage | ISO 294-4 | 0.4–0.7 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (UL94) | - |
| UV resistance | - | Very Good | - |
| Chemical resistance | - | Good | - |
| Flame retardant rating 3,0mm | - | HB (UL94) | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | HB | - |