TPU FLEX Semisoft has been specially developed for the FDM/FFF process. Based on Polycaprolactone-Polyester, it offers an extensibility of up to 550%, high material quality, high chemical resistance, and a heat distortion resistance of up to 98°C, making the material suitable for numerous industrial applications. The raw material is compliant with REACH and RoHS standards.
Free from halogens, meeting stricter material safety standards for sensitive industrial applications.
Exceptionally strong bonding between layers, even beyond what's typical for flexible filaments.
Independently tested for UV and weather resistance, holding its colour and integrity through extended outdoor exposure.
Genuine toughness against impact and breakage, built for parts that need to survive real-world knocks, not just flex.
From standard FDM printers to AMS and multi-material setups, Extrudr filament is built to work reliably with the printer you already own.
From the Austrian Alps, every Extrudr spool is manufactured with care, precision and strict EU standards.
FLEX Semisoft is compatible with all standard FDM printers on the market.
No. FLEX Semisoft prints reliably with a standard nozzle.
Yes. FLEX Semisoft is fully compatible with AMS (Automatic Material System) solutions, including the Bambu Lab AMS.
Yes. FLEX Semisoft is a hygroscopic material and should be dried before printing to achieve optimal print quality. We recommend drying for 12 hours at 60°C.
Yes. FLEX Semisoft is UV-resistant, making it suitable for outdoor and light-exposed applications.
Yes. FLEX Semisoft offers high chemical resistance, suited to demanding industrial applications.
No. FLEX Semisoft is not certified for food contact.
Compliance applies to the raw material, not the finished printed part. Any part intended for a regulated application must undergo separate certification by an accredited third-party laboratory. Requirements vary depending on intended use and applicable standards.
Store FLEX Semisoft in a dry room at room temperature (18–27°C / 65–80°F). Stored neatly, it is protected from dust and sunlight.
When stored correctly, FLEX Semisoft has a shelf life of 2 years.
UP TO 1000 MM/S
Recommended settings for printers with a 0.4 mm nozzle. Max. 50% layer height. Optimal settings may vary between printers and are also dependent on environmental factors.
Our material profiles make printing easier and more reliable. The profiles are perfectly optimised for Extrudr filaments and deliver perfect results straight away. Simply select your printer and material, import the profile into your slicer, and you’re ready to go.
| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 60 MPa | Typical |
| Tensile strength at yield | ISO 527-1 | 36 MPa | Typical |
| Tensile stress at break | ISO 527-1 | 36 MPa | Very Good |
| Elongation at break | ISO 527-1 | 504 % | Outstanding |
| Flexural modulus | ISO 178 | 55 MPa | Typical |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | No Break (NB) {ISO 179-1eA} | - |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Vicat softening temp. (VST/B50) | ISO 306 | ~68 °C | Typical |
| Melting point (Tm) | ISO 3146-C | 180–230 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | -34 °C | - |
| Thermal decomposition temp. | - | 230 °C | Typical |
| CLTE — flow direction | - | 1.5 cm/cm/°C | Typical |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.17 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.8 % | - |
| Mould shrinkage | ISO 294-4 | 0.8–1.2 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| UV resistance | - | Yes | - |
| Chemical resistance | - | Yes | - |
| Abrasion resistance | - | 25 mm³ | - |