UP TO 1000 MM/S| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 5000 MPa | - |
| Tensile strength at yield | ISO 527–1/-2 | 59 MPa ±0.4 | - |
| Tensile stress at break | ISO 527-1 | 62 MPa | Typical |
| Elongation at break | ISO 527-1 | 3 % | Typical |
| Flexural modulus | ISO 178 | 3800 MPa | - |
| Flexural strength | ISO 178 | 88 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 5 kJ/m² | Typical |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 3.5 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 22 kJ/m² | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 16 kJ/m² | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 5 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 1700 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 73 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 68 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 76 °C | - |
| Melting point (Tm) | ISO 3146-C | Amorphous (no Tm) {ISO 3146-C} | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 80 °C | - |
| Melt flow rate (MFR) — 210°C/2.16 kg | - | 5 g/10 min {ISO 1133-1 | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 35 cm³/10 min | Very Good |
| Thermal decomposition temp. | - | 370 °C | - |
| CLTE — flow direction | - | 0.4 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.31 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | < 0.1 % | - |
| Mould shrinkage | ISO 294-4 | 0.2–0.3 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| UV resistance | - | Good | - |
| Chemical resistance | - | Good | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | (not tested) | - |