| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 4100 MPa | - |
| Tensile strength at yield | ISO 527-1 | 58 MPa | - |
| Tensile stress at break | ISO 527-1 | 55 MPa | Typical |
| Elongation at break | ISO 527-1 | 2.5 % | Typical |
| Flexural modulus | ISO 178 | 4000 MPa | - |
| Flexural strength | ISO 178 | 88 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 7 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 5 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 25 kJ/m² | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 18 kJ/m² | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 4 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 1900 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 96 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 84 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 97 °C | - |
| Melting point (Tm) | ISO 3146-C | 210–250 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 103 °C | - |
| Melt flow rate (MFR) — 210°C/2.16 kg | - | 2 g/10 min {ISO 1133-1 | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 12 cm³/10 min | Good |
| Thermal decomposition temp. | - | 350 °C | - |
| CLTE — flow direction | - | 0.55 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.13 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.8 % | - |
| Mould shrinkage | ISO 294-4 | 0.3 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (UL94) | - |
| UV resistance | - | Good | - |
| Chemical resistance | - | Good | - |
| Flame retardant rating 3,0mm | - | HB (UL94) | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | HB (1.5 mm) | - |