DuraPro PA12 is a highly functional polyamide (nylon) built for industrial applications. It's characterised by exceptionally high impact and notched impact strength, retaining toughness even at low temperatures, alongside very good heat resistance. Low moisture absorption keeps parts dimensionally stable over time, a genuine advantage of PA12 over other nylon grades, while excellent chemical resistance and easy handling make it a dependable choice for demanding, real-world 3D printing projects.
DuraPro PA12
SKU: 9010241542024
Material
DuraPro PA12color
black | RAL 9017Filament diameter
1.75 mmCoil
0.7 kgincl. VAT
45,82 €
incl. VAT
45,82 €
In Stock
Made in Austria
Secure Checkout With
Engineered for Industrial Demands
IDEAL FOR
- Automotive & Industrial Components
- Jigs, Fixtures & Tooling
- Electrical Insulation & Enclosures
- Parts Exposed to Chemicals or Cold
DuraPro PA12 Highlights
HIGH IMPACT STRENGTH
Retains toughness even at -30°C, with no break in unnotched impact testing at both room and sub-zero temperatures.
LOW MOISTURE ABSORPTION
Just 1.6% water absorption at saturation, significantly lower than other nylon grades, keeping parts dimensionally stable over time.
HIGH HEAT RESISTANCE
Improved thermal performance over the standard blend, holds its shape reliably under serious thermal stress.
GOOD CHEMICAL RESISTANCE
Withstands exposure to a broad range of chemicals, suited to demanding industrial environments.
FITS ANY PRINTER, ANY SYSTEM
From standard FDM printers to AMS and multi-material setups, Extrudr filament is built to work reliably with the printer you already own.
MADE IN AUSTRIA
From the Austrian Alps, every Extrudr spool is manufactured with care, precision and strict EU standards.
Nozzle temperature 260–290 °C
Build plate temperature 110 °C
Surface preparation Recommended
Speed < 150
Cooling fan 0–50 %
Enclosed chamber required Yes
Hardened nozzle required No
Max. volumetric flow rate 8 mm³/s
Recommended settings for printers with a 0.4 mm nozzle. Max. 50% layer height. Optimal settings may vary between printers and are also dependent on environmental factors.
Drying temperature 65 °C
Drying time 8–12 h
Our material profiles make printing easier and more reliable. The profiles are perfectly optimised for Extrudr filaments and deliver perfect results straight away. Simply select your printer and material, import the profile into your slicer, and you’re ready to go.
| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 1500 MPa | Very Good |
| Tensile strength at yield | ISO 527-1 | 50 MPa | Good |
| Elongation at break | ISO 527-1 | > 50 % | - |
| Flexural modulus | ISO 178 | 1300 MPa | Very Good |
| Flexural strength | ISO 178 | 45 MPa | Typical |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 11 kJ/m² | Very Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 6 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 60 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 4800 N | Outstanding |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 135 °C | Excellent |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 55 °C | Typical |
| Vicat softening temp. (VST/B50) | ISO 306 | 142 °C | Excellent |
| Melting point (Tm) | ISO 3146-C | 180 °C | Typical |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 45 °C | Typical |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 8 cm³/10 min | Good |
| Thermal decomposition temp. | - | ~>> 300 °C | - |
| CLTE — flow direction | - | 0.0001 cm/cm/°C | Outstanding |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.01 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 1.6 % | Excellent |
| Mould shrinkage | ISO 294-4 | 1 % | Typical |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (1.6 mm) (UL94) | - |
| Chemical resistance | - | Good | - |
| Electrical Properties | Method | Value | Rating |
|---|---|---|---|
| Specific surface resistance | - | 100000000000000 Ω | - |
| Specific volume resistivity | - | 100000000000000 Ω·cm | - |
| Dielectric strength | - | 30 kV/mm | - |
| Comparative tracking index (CTI) | - | 600 V | - |
PRINTING & COMPATIBILITY
DuraPro PA12 is compatible with all standard FDM printers on the market. Note: an enclosed print space is required, and a heated bed capable of reaching 110°C is recommended, printers without these capabilities may not achieve optimal results.
Yes. DuraPro PA12 is fully compatible with AMS (Automatic Material System) solutions, including the Bambu Lab AMS.
No. DuraPro PA12 prints reliably with a standard nozzle.
Yes. DuraPro PA12 is a hygroscopic material and should be dried before printing to achieve optimal print quality. We recommend drying for 8–12 hours at 65°C.
MATERIAL PROPERTIES
DuraPro PA12 offers significantly lower moisture absorption than PA6-based nylons (1.6% vs. typically around 9-10% at saturation), giving it better long-term dimensional stability. This makes it easier to store and print reliably, with less risk of warping from humidity.
Yes. DuraPro PA12 is suitable for outdoor use.
CERTIFICATION & COMPLIANCE
No. DuraPro PA12 is not suitable for food contact.
CARE & STORAGE
Store DuraPro PA12 in a dry room at room temperature (18–27°C / 65–80°F). Stored neatly, it is protected from dust and sunlight.
When stored correctly, DuraPro PA12 has a shelf life of 2 years.
–