| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 6200 MPa | - |
| Tensile strength at yield | ISO 527–1/-2 | 70.2 MPa | - |
| Tensile stress at break | ISO 527-1 | 90 MPa | Typical |
| Elongation at break | ISO 527-1 | 3 % | Typical |
| Flexural modulus | ISO 178 | 6000 MPa | - |
| Flexural strength | ISO 178 | 130 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 11 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 8 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 40 kJ/m² | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 30 kJ/m² | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 8 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 2400 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 115 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 112 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 130 °C | - |
| Melting point (Tm) | ISO 3146-C | 220 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 145 °C | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 5 cm³/10 min | Typical |
| Thermal decomposition temp. | - | > 390 °C | - |
| CLTE — flow direction | - | 0.35 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.25 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.5 % | - |
| Mould shrinkage | ISO 294-4 | 0.3–0.5 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (UL94) | - |
| Chemical resistance | - | Very Good | - |
| Flame retardant rating 3,0mm | - | HB (UL94) | - |
| Electrical Properties | Method | Value | Rating |
|---|---|---|---|
| Specific surface resistance | - | 10³–10⁶ Ω (conductive – measure) | - |
| Specific volume resistivity | - | 10³–10⁶ Ω·cm (conductive – measure) | - |
| Dielectric strength | - | (conductive) | - |
| Comparative tracking index (CTI) | - | (conductive) | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | HB (1.5 mm) | - |
| Glow wire flammability index (GWFI) | - | (not measured) | - |
| Limiting oxygen index (LOI) | - | 21 % | - |