| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 6000 MPa | - |
| Tensile strength at yield | ISO 527-1 | 120 MPa | - |
| Tensile stress at break | ISO 527-1 | 115 MPa | Typical |
| Elongation at break | ISO 527-1 | 3 % | Typical |
| Flexural modulus | ISO 178 | 5750 MPa | - |
| Flexural strength | ISO 178 | 160 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 7 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 5 kJ/m² | Typical |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 55 kJ/m² | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | 35 kJ/m² | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 170 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 145 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 178 °C | - |
| Melting point (Tm) | ISO 3146-C | 182 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 55 °C | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 3 cm³/10 min | Typical |
| Thermal decomposition temp. | - | > 300 °C | - |
| CLTE — flow direction | - | 0.45 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.17 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 9.2 % | Typical |
| Mould shrinkage | ISO 294-4 | 0.3–0.5 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (1.6 mm) (UL94) | - |
| Chemical resistance | - | Very Good | - |