| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 2200 MPa | - |
| Tensile strength at yield | ISO 527-1 | 60 MPa | - |
| Tensile stress at break | ISO 527-1 | 50 MPa | Typical |
| Elongation at break | ISO 527-1 | > 50 % | - |
| Flexural modulus | ISO 178 | 2150 MPa | - |
| Flexural strength | ISO 178 | 80 MPa | - |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 60 kJ/m² | Good |
| Charpy notched impact strength (-30°C) | ISO 179-1eA | 40 kJ/m² | Good |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Charpy unnotched impact strength (-30°C) | ISO 179-1eU | No Break (NB) {ISO 179-1eU} | - |
| Puncture maximum energy (-30°C) | ISO 6603-2 | 58 J | - |
| Multiaxial instrumented impact, peak force (-30°C) | ISO 6603-2 | 5000 N | - |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 110 °C | - |
| Heat deflection temp. (HDT/A) — 1.8 MPa | ISO 75-1 | 85 °C | - |
| Vicat softening temp. (VST/B50) | ISO 306 | 126 °C | - |
| Melting point (Tm) | ISO 3146-C | 220 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | 145 °C | - |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 18 cm³/10 min | Good |
| Thermal decomposition temp. | - | > 350 °C | - |
| CLTE — flow direction | - | 0.9 cm/cm/°C | - |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.2 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.5 % | - |
| Mould shrinkage | ISO 294-4 | 0.7–0.9 % | - |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| Flame retardant rating 1.5mm | - | HB (UL94) | - |
| Chemical resistance | - | Excellent | - |
| Flame retardant rating 3,0mm | - | HB (UL94) | - |
| Electrical Properties | Method | Value | Rating |
|---|---|---|---|
| Specific surface resistance | - | 100000000000000000 Ω | - |
| Specific volume resistivity | - | 100000000000000000 Ω·cm | - |
| Dielectric strength | - | 30 kV/mm | - |
| Comparative tracking index (CTI) | - | Stage 600 | - |
| Fire & Compliance | Method | Value | Rating |
|---|---|---|---|
| Flammability rating (UL 94) | - | HB (1.5 mm) | - |
| Glow wire flammability index (GWFI) | - | 750 °C | - |