Tensile modulus (Young's modulus)

Test/Property Method

Test/Property Numeric Value

Test/Property Tolerance Type

Test/Property Tolerance Value

Test/Property Unit

3100 ±46 MPa (ISO 527–1/-2)

Tensile strength at yield

53 ±0.2 MPa (ISO 527–1/-2)

Tensile stress at break

Elongation at break

7.6 ±1.1 % (ISO 527–1/-2)

Flexural modulus

Charpy notched impact strength (+23°C)

Test/Property Comparable

Test/Property Max Value

Test/Property Min Value

Test/Property Note

1.7 ±0.4 kJ/m² (ISO 180)

Vicat softening temp. (VST/B50)

85 °C (ISO 306/A50)

Melting point (Tm)

Melt flow rate (MFR) — 210°C/2.16 kg

Density

1.41 g/cm³ (ISO 1183–1)

Mould shrinkage

Nozzle temperature

210–240 °C

Build plate temperature

60–90 °C

Surface preparation

Not required

Print speed

20–200 mm/s

Cooling fan

20–50 %

Enclosed chamber required

For larger components

Hardened nozzle required

Max. volumetric flow rate

12 mm³/s

Drying temperature

60 °C

Drying time

4–6 h

Flexural strength

Heat deflection temp. (HDT/B) — 0.45 MPa

67 °C (ISO 75–2/B)

Thermal decomposition temp.

Flame retardant rating

UV resistance

Chemical resistance

Abrasion resistance

ESD safe

Flammability rating (UL 94)

V-2 (3.2 mm) (UL 94)

Charpy notched impact strength (-30°C)

Charpy unnotched impact strength (-30°C)

Heat deflection temp. (HDT/A) — 1.8 MPa

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

78 ±6 kJ/m² (ISO 180)

Puncture maximum force (-30°C)

Multiaxial instrumented impact, peak force (-30°C)

Melt volume rate (MVR) — 235°C/5.0 kg

CLTE — flow direction

Water absorption (saturation, 23°C)

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

Filaments

Standard

Material

XPETG MATT

Color

black

Filament diameter

1.75 mm

Coil

1 kg

XPETG MATT black 1.75 mm 1 kg

XPETG MATT has been developed for a wide range of applications where the main requirement is a good balance between optical and mechanical material properties. In addition, it is more thermally resistant than normal PETG. The raw material is certified according to FDA, REACH and RoHS standards.

Filament

XPETG MATT is a 100% recyclable 3D printing filament with a matte finish, developed for applications requiring optical and mechanical performance. Thermally resistant, free from warping and shrinking, it prints efficiently at 210–230 °C. Approved according to FDA, REACH, and RoHS.

XPETG MATT Filament – Matte Surface and 100% Recyclable 

2.85 mm

XPETG MATT red 2.85 mm 1 kg

blue

XPETG MATT blue 2.85 mm 1 kg

metallic

XPETG MATT metallic 2.85 mm 1 kg

military green

XPETG MATT military green 2.85 mm 1 kg

white

2.5 kg

XPETG MATT white 1.75 mm 2.5 kg

XPETG MATT black 1.75 mm 2.5 kg

XPETG MATT blue 1.75 mm 2.5 kg

XPETG MATT red 1.75 mm 2.5 kg

anthracite

XPETG MATT anthracite 1.75 mm 2.5 kg

XPETG MATT metallic 1.75 mm 2.5 kg

XPETG MATT military green 1.75 mm 2.5 kg

XPETG MATT blue 1.75 mm 1 kg

XPETG MATT red 1.75 mm 1 kg

XPETG MATT military green 1.75 mm 1 kg

XPETG MATT anthracite 1.75 mm 1 kg

XPETG MATT metallic 1.75 mm 1 kg

XPETG MATT black 2.85 mm 1 kg

XPETG MATT white 2.85 mm 1 kg

XPETG MATT white 1.75 mm 1 kg

orange

XPETG MATT orange 1.75 mm 1 kg

XPETG MATT orange 1.75 mm 2.5 kg

XPETG MATT

Material

Farbe

Filament-Durchmesser

Spule

Artikel-nr

Suche

XPETG MATT

Material

Farbe

Filament-Durchmesser

Spule

Artikel-nr