Tensile modulus (Young's modulus)

Test/Property Method

Test/Property Numeric Value

Test/Property Unit

5000 MPa {ISO 527-1}

Tensile strength at yield

Test/Property Tolerance Type

Test/Property Tolerance Value

59 ±0.4 MPa {ISO 527–1/-2}

Tensile stress at break

62 MPa {ISO 527-1}

Elongation at break

3 % {ISO 527-1}

Flexural modulus

3800 MPa {ISO 178}

Charpy notched impact strength (+23°C)

5 kJ/m² {ISO 179-1eA}

Vicat softening temp. (VST/B50)

76 °C {ISO 306}

Melting point (Tm)

Test/Property Note

Amorphous (no Tm) {ISO 3146-C}

Melt flow rate (MFR) — 210°C/2.16 kg

5 g/10 min {ISO 1133-1 (210°C/2.16 kg})

Density

1.31 g/cm³ {ISO 1183-1}

Mould shrinkage

Test/Property Max Value

Test/Property Min Value

0.2–0.3 % {ISO 294-4}

Nozzle temperature

220–250 °C

Build plate temperature

60–90 °C

Surface preparation

Not required

Print speed

20–200 mm/s

Cooling fan

20–50 %

Enclosed chamber required

For larger components

Hardened nozzle required

Max. volumetric flow rate

10 mm³/s

Drying temperature

60 °C

Drying time

4–6 h

Flexural strength

88 MPa {ISO 178}

Heat deflection temp. (HDT/B) — 0.45 MPa

73 °C {ISO 75-1}

Thermal decomposition temp.

370 °C

UV resistance

Good

Chemical resistance

Abrasion resistance

ESD safe

Flammability rating (UL 94)

(not tested)

Charpy notched impact strength (-30°C)

3.5 kJ/m² {ISO 179-1eA}

Charpy unnotched impact strength (-30°C)

16 kJ/m² {ISO 179-1eU}

Heat deflection temp. (HDT/A) — 1.8 MPa

68 °C {ISO 75-1}

Glow wire flammability index (GWFI)

Glow wire ignition temperature (GWIT)

Limiting oxygen index (LOI)

Charpy unnotched impact strength (+23°C)

22 kJ/m² {ISO 179-1eU}

Multiaxial instrumented impact, peak force (-30°C)

1700 N {ISO 6603-2}

Melt volume rate (MVR) — 235°C/5.0 kg

35 cm³/10 min

CLTE — flow direction

0.4 cm/cm/°C

Water absorption (saturation, 23°C)

Testproperty Prefix

< 0.1 %

Specific surface resistance

Specific volume resistivity

Dielectric strength

Comparative tracking index (CTI)

Glass transition temp. (Tg)

80 °C {ISO 11357-1 (DSC)}

Ease of printing

Visual quality

Layer adhesion

Puncture maximum energy (-30°C)

5 J {ISO 6603-2}

Flame retardant rating 1.5mm

Flame retardant rating 3,0mm

Filaments

Standard

Material

XPETG CF

Color

black

Filament diameter

1.75 mm

Coil

0.8 kg

XPETG CF black 1.75 mm 0.8 kg

XPETG CF has been developed for a wide range of applications where the main requirement is a good balance between mechanical and optical material properties. The raw material is certified according to REACH and RoHS standards. PETG is flame retardant according to UL 94 with a wall thickness of 3.2 mm.

Filament

XPETG CF is a carbon fiber-reinforced 3D printing filament developed for a wide range of applications. It offers excellent mechanical properties and chemical resistance, low warping and shrinkage, and is flame retardant (UL 94). Approved according to REACH and RoHS standards.